　  輕燒鎂球供到廠里時要及時, 防止了耐火材料受潮或貯存時間過長。砌磚進程中, 對掉角、缺棱、表面由裂縫、磚形不整的磚材堅決不運用, 并且對砌筑質量進行把關,終究對砌筑作業進行查驗。保證了砌筑質量?！　?/p>

    在正常生產中, 要維護窯磚, 實際上便是對窯皮的維護,應盡悉數或許, 堅持工況安穩, 維護好窯皮，需求采取維護措施，總結以下幾點：
　　
　　1.加強機械、電氣設備的維護, 加強崗位人員、車間技術人員的巡檢, 發現問題及時調整處理, 以保證設備的完好率和作業率。
　　
　　2.加強技術操作, 優化操作參數, 安穩熱工原則, 安穩系統工況,減小波動, 防止系統一再開停。
　　
　　3.做好系統漏風密封處理, 安穩入窯生料喂料量;
　　
　　4.選用低溫煅燒技術, 控制分化爐出口溫度870～880℃, 出口廢氣溫度控制在300～330℃。
　　
　　5.安穩配料計劃, 控制生料成分
　　
　　6.控制適宜的煤粉細度及水分。
　　
　　7.加強原材料進廠控制, 強化預均化作用, 嚴控原材料的堿含量。堿含量多, 窯內結圈一再, 窯皮掛、掉一再, 耐火磚的磨損、爆裂加重,影響運用周期。

Protective measures should be taken after purchasing lightly burned magnesium balls

 Light-burned magnesium balls should be supplied to the factory in time to prevent the refractory material from being dampened or stored for too long. In the process of bricklaying, we must not use bricks with corners, edges, cracks, and irregular brick surfaces. We also check the quality of the masonry and check the masonry after all. Guaranteed masonry quality.

 In normal production, the maintenance of kiln bricks is actually the maintenance of the kiln skin. You should do everything possible, adhere to the stable working conditions, maintain the kiln skin, and take maintenance measures to summarize the following points:

1. Strengthen the maintenance of machinery and electrical equipment, strengthen inspections of post personnel and workshop technicians, and adjust and deal with problems in time to ensure the integrity and operating rate of equipment.

2. Strengthen technical operations, optimize operating parameters, stabilize thermal principles, stabilize system operating conditions, reduce fluctuations, and prevent the system from repeatedly starting and stopping.

3. Seal the air leakage of the system well and stabilize the feed amount of raw material into the kiln;

4. Select low-temperature calcination technology to control the outlet temperature of the differentiation furnace from 870 to 880 ° C and the outlet exhaust gas temperature to be controlled from 300 to 330 ° C.

5. Stable ingredients plan, control raw ingredients

6. Control the appropriate fineness and moisture of pulverized coal.

7. Strengthen the control of raw materials entering the plant, strengthen the pre-homogenization, and strictly control the alkali content of raw materials. The alkali content is too large, the kiln ring is repeatedly formed, the kiln skin is hung and dropped, the abrasion and burst of the refractory bricks are aggravated, which affects the operating cycle.